СПЕКАНИЕ И ПРОЧНОСТЬ СТЕНОВОЙ КЕРАМИКИ И ФАЯНСА ИЗ КОМПОЗИЦИЙ ГЛИНИСТОГО И ДИОПСИДСОДЕРЖАЩЕГО СЫРЬЯ

The paper summarizes the research results of sintering and durability of wall ceramic materi-als modified by diopside-containing raw products and based on low-melting-point clays and loams, and kaolinand high-melting-point clay faience. Mechanical-and-physical properties of ceramic materials are identified and studied after annealing, depending on the diopside content. It is shown that depending on the content and introduction of clay minerals in the ceramic mixture, both coarse (0.5–1 mm) and fine (0.06 mm, dominating particle size of 0.01–0.015 mm) dis-persed diopside particles can be used. It is found that for loams with the clay mineral content of less than 10 wt.%, the addition of finely-dispersed diopside particles is more efficient. The latter provides ceramic sintering at 1000–1100 °С and increases its strength by 1.5–2 times. The intro-duction of dispersion diopside particles in the faience mixture lowers the annealing temperature from 1250 to 1150 °С with a simultaneous increase in its strength.