Microstructure of Cr100−xAlx alloys (10 at% ⪅ x ⪅ 33 at%) studied by means of transmission electron microscopy and diffraction. I. Microstructure of the β‐phase

As part of a study on the microstructure of Cr100–xAlx alloys (10 at% ⪅ x ⪅ 33 at%) results are reported on the β-phase (26 at% ⪅ x ⪅ 33 at%) since they bear a relationship with the microstructure in the wider composition range. From a crystallographic analysis of the structure, models are proposed for the defects of chemical as well as magnetic nature. Electron microscopy and diffraction observations are analysed in terms of these models and confirm the proposals. High resolution microscopy is used for a detailed analysis of the interfaces between domains down to an atomic scale. Diffuse intensity contours observed in the diffraction patterns of alloys with 20 at% ⪅ x ⪅ 26 at% Al are interpreted in terms of a transition state of the β-phase. Als Teil einer Untersuchung zur Mikrostruktur von Cr100–xAlx-Legierungen (10 At% ⪅ x ⪅ 33 At%) werden die Ergebnisse an der β-Phase (26 At% ⪅ x ⪅ 33 At%) mitgeteilt, da sie eine Beziehung mit der Mikrostruktur in einem weiteren Zusammensetzungsbereich enthalten. Aus der kristallograephischen Analyse der Struktur werden Modelle fur chemische sowie auch magnetische Defekt vorgeschlagen. Elektronenmikroskopische und Beugungsmessungen werden mit diesen Modellen analysiert und bestatigen diese Vorschlage. Hochauflosende Mikroskopie wird fur eine ausfuhrliche Analyse der Grenzflachen zwischen Domanen bis zu atomaren Abmessungen herab benutzt. Die in den Beugungsdiagrammen von Legierungen mit 20 At % ⪅ x ⪅ 26 At% Al beobachteten diffusen Intensitatskonturen werden mit einem Ubergangszustand der β-Phase gedeutet.