Effect of severe plastic deformation on an extruded ZK60 magnesium alloy

Equal channel angular pressing (ECAP) was carried out on extruded ZK60 magnesium alloy until an equivalent strain of ∼4 (corresponding to 4 passes) at 523K following route Bc. The effect of the deformation on both microstructure and texture was investigated by analysis of inverse pole figures and pole figures respectively, determined by EBSD. Additionaly, the mechanical properties were evaluated through tensile tests. The ECAPed processed ZK60 alloy showed the presence of dynamic recrystallization (DRX) process, correlated with a strong basal fiber texture. The presence of pyramidal slip was also observed, which can be correlated with the presence on twin-oriented boundaries in the material. Both the grain size reduction and the existence of texture influenced the ductility of the magnesium alloy processed by ECAP, as the ductility of the ZK60 alloy after four ECAP passes increased two times in comparation with the initial (un-processed) material.