Low Temperature Aqueous Electrodeposited TiOx Thin Films as Electron Extraction Layer for Efficient Inverted Organic Solar Cells

Organic solar cells based on poly(3-hexylthiophene) and [6,6]-phenyl-C61-butyric acid methyl ester were fabricated with electrodeposited TiOx electron extraction layers 5–180 nm thick. Electrodeposition under ambient conditions is an attractive, facile and viable approach to prepare metal oxide interfacial layers. The TiOx films obtained displayed a linear relationship between thickness and deposition time when fabricated under ambient conditions using an aqueous air stable peroxotitanium precursor. The precursor solution was prepared from titanium isopropoxide using a chelate process, which allowed water to be used as solvent due to considerably decreased sensitivity of the precursor solution towards hydrolysis. Highly conformal TiOx films, typically observed with vacuum deposition techniques, were obtained on the indium tin oxide substrate upon electrogeneration of OH– ions using H2O2 additive. Conversely, significantly rougher films with spherical growths were obtained using NO3– additives. Low tempera...