Preparation of nanostructured Ni/Al2O3 composite coatings in high magnetic field

Abstract Ni/Al 2 O 3 composite coatings were prepared by a novel method from a modified Watt's type electrolyte containing nano-Al 2 O 3 particles, where a high magnetic field was imposed in the direction parallel to an electrolytic current instead of mechanical agitation. Effects of magnetic field on the content of particles, surface morphology, microhardness and wear resistance of plating layer were investigated. It was found that the high magnetic field played an important role in the formation of composite coatings. The amounts of nano-Al 2 O 3 particles in the composite coating increased with increasing of magnetic flux density and reached a maximum value at 8 T, then reduced slightly. The microhardness and wear resistance of the nanocomposite coatings also enhanced with increasing of magnetic flux density as compared to that of pure Ni coating fabricated in the absence of magnetic field. That was because the co-deposited nano-Al 2 O 3 particles were uniformly distributed in the Ni matrix and contributed to greatly increase the microhardness and wear resistance of the composite coatings. Moreover, the mechanism of action of high magnetic field was discussed preliminarily.