Physical origins of high photoluminescence quantum yield in α-CsPbI3 nanocrystals and their stability
2020
Abstract CsPbI3 nanocrystals (NCs) with photoluminescence quantum yield (PLQY) larger than 90% have been synthesized at different temperature regions, and the physical origins for high PLQY were investigated. HRTEM images show that cubic phase CsPbI3 (α-CsPbI3) is surrounded by hexagonal Cs4PbI6 in the low temperature region, and the ratio of CsPbI3 and Cs4PbI6 increases with increasing the reaction temperature. The strong confinement effect of Cs4PbI6 leads to the high PLQY (95%) of α-CsPbI3 NCs when the reaction temperature is 120 oC. The confinement effect of Cs4PbI6 is weakened with increasing reaction temperature, which leads to the decrease of PLQY at 140 oC. However, non-radiative recombination is suppressed due to the microstructure improvement with further increasing the reaction temperature, and PLQY as high as 97% is achieved at 180 oC. Stability testing shows that fast degradation of α-CsPbI3 NCs occurs in low reaction temperature region, and α-CsPbI3 NCs with high PLQY can be stored in air for 90 days when the reaction temperature is 180 oC .
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
35
References
5
Citations
NaN
KQI