Compressive strength of directionally solidified NiAl-NiAlNb intermetallics at 1200 and 1300 K

Results are presented from measurements of 1200 K and 1300 K compressive properties of two directionally solidified NiAl-NiAlNb compositions (in at. pct): Ni-41.75Al-16.5Nb (eutectic composition) and Ni-47.5Al-8.9Nb-1.3C (Al-rich composition). Results showed that the strength of the eutectic was a factor of 2 greater than that of the Al-rich composition. However, the analysis of the compressive stress-strain data indicated that the deformation mechanism was the same in both materials. 15 refs.