Multi-tube tantalum membrane reactor for HIx processing section of IS thermochemical process

Abstract HIx processing section of Iodine-Sulphur (IS) thermochemical cycle dictates the overall efficiency of the cycle, which poses extremely corrosive HI–H2O–I2 environment, coupled with a very low equilibrium conversion (~22%) of HI to hydrogen at 450 °C. Here, we report the fabrication, characterization and operation of a 4-tube packed bed catalytic tantalum (Ta) membrane reactor (MR) for enhanced HI decomposition. Gamma coated clay-alumina tubes were used as supports for fabrication of Ta membranes. Clay-alumina base support was fabricated with 92% alumina (~8 μm particle size) and 8% clay (~10 μm particle size), sintered at a temperature of 1400 °C. An intermediate gamma alumina coating was provided with 4% polyvinyl butyral as binder for a 10% solid loading. Composite alumina tubes were coated with thin films of Ta metal of thickness 80% single-pass conversion of HI to hydrogen at 450 °C. The hydrogen throughput of the reactor was ~30 LPH at a 2 bar trans-membrane pressure, with >99.95% purity. This is the first time a muti-tube MR is reported for HIx processing section of IS process.