Stiffness reductions during tensile fatigue testing of graphite/epoxy angle-ply laminates

The monitoring of modulus decay during fatigue testing as an indicator of damage accumulation and incipient failure has frequently been postulated. The present study was designed to generate tensile fatigue data under carefully controlled test conditions. A computerized data acquisition system was used to permit the measurement of dynamic modulus without interrupting the fatigue cycling. Two different 8-ply laminate configurations, viz, (+ or - 45)2s and (+ or - 67.5)2s, of a T300/5208 graphite/epoxy composite were tested. The (+ or 45)2s laminate did exhibit some modulus decay, although there was no well-defined correlation with applied stress level or number of cycles. The (+ or - 67.5)2s laminate did not exhibit any measurable modulus decay. Secondary effects observed included a slight recovery of the modulus decay after a test interruption, and a significant viscoelastic (creep) response of the (+ or - 45)2s laminate during fatigue testing.