NANOSTRUCTURE TITANIA REINFORCED CONDUCTING POLYMER COMPOSITES

Composites of polyaniline with synthesized nanostructured titania (TiO2) and polyaniline with commercial TiO2 have been in situ synthesized by oxidative chemical polymerization method. Sulfuric acid was used as dopant during the polymerization process. Sol-gel precipitates of nanostructured titania were synthesized by hydrolyzing the mixture of titanium chloride (TiCl3) and colloidal transparent solution of starch. Composite materials were subjected for comparison to spectroscopic and X-ray diffraction analysis. Strong coupling/interaction of titania with the imine nitrogen in polyaniline confirmed by FTIR spectral analysis. XRD shows the composite of synthesized titania with polyaniline have broaden peak as compared to that of commercial titania with polyaniline indicating particle size in the range of nanometer scale which is supported by 40 nm particle size of the synthesized titania from TEM picture. Increase in conductivity with increasing temperature was observed in both the composite materials.