Thermal Fatigue Reliability of Solder Joints in a Thin Film Optical Filter Device

Plastic and creep deformations of solder joints during thermal cycling are the main factors of misalignments and power losses in optical telecommunication components. Furthermore, the increased mismatch between solder Joint-bonded areas may cause severe failure in the components. Darveaux`s creep model was implemented into a finite element program (ABAQUS) to simulate creep response of solder. Based on the finite element results, thermal fatigue reliability was predicted by using various fatigue life prediction models. Also, the effects of ramp conditions, dwelling time, and solder joint-embedding materials on the reliability were investigated under the thermal cycling conditions of the Telcordia schedule (-40∼75).