13 C Solid State NMR Study of the PVC/PEO/GYPSUM SYSTEM

Solid state nuclear magnetic resonance spectroscopy (NMR) was used as one of the instrumental method that permits a direct identification of the miscibility of polymer blend components. As a consequence, it also permits to evaluate the homogeneity of the blends at the molecular level. Polymer blends can be used in several applications, thus, it is necessary to have complete understanding of the chemical and dynamic behavior of their components. In this work the solid state NMR results showed that in the system formed by poly (vinyl chloride) (PVC), poly(ethylene oxide) (PEO) and gypsum (PVC/PEO/Gypsum), PEO acts as a plasticizer, but a phase separation occurs due to the weak specific intermolecular interactions among the blend components. Complementary surface information on these blends was obtained by X-Ray Photoelectron Spectroscopy (XPS). From this, it was observed that the blends surface was covered by a continuous PEO layer. Resumo: Ressonância magnetica nuclear no estado solido (RMN-MAS) foi usada como um metodo instrumental que permitiu a identificacao direta da miscibilidade dos componentes numa blenda polimerica. Como consequencia, foi possivel avaliar a homogeneidade das blendas em nivel molecular. As blendas polimericas podem ser usadas em diferentes aplicacoes, assim, torna-se necessario ter um completo entendimento do comportamento quimico e dinâmico de seus componentes. Neste trabalho os resultados da RMN de estado solido mostraram que o sistema formado por poli(cloreto de vinilia) (PVC), poli(oxido de etileno) (PEO) e gesso (PVC/PEO/Gesso), PO age como um plastificante polimerico, porem ocorreu separacao de fase devido as fracas interacoes intermoleculares entre os componentes a blenda. Dados complementares sobre estas blendas foram obtidos pela tecnica de raio X de superficie (XPS), em que foi observado que na blenda a superficie esta recoberta pelo PEO como uma fase continua e fina .