Li0.95Na0.05Ti2(PO4)3/C with Good Performance as Anode Material for Aqueous Rechargeable Lithium Batteries

Li0.95Na0.05Ti2(PO4)3/C nanocomposite was prepared by sol-gel method.The structure and morphology of the samples were characterized by XRD, SEM which showed the particles had typical NASICON structure and diameter range from 400~500nm. The electrochemical performance were tested by cyclic voltammetry and galvanostatic charge–discharge. Results show Li0.95Na0.05Ti2(PO4)3/C nanocomposite exhibitsmuch better electrochemical performance than bare Li0.95Na0.05Ti2(PO4)3.