Shock-driven depolarization behavior in BNT-based lead-free ceramics

The pulsed power supply that generates megawatts of electrical power has drawn important attention for many decades. Despite that the large energy output has been obtained in lead-containing materials such as Pb(Zr0.95Ti0.05)O3 (PZT95/5) ceramics, lead-free ferroelectric candidates are highly desired due to the environmental concerns. In this work, we report the depolarization behavior of lead-free ternary 0.99[0.98(Bi0.5Na0.5)(Ti0.995Mn0.005)O3-0.02BiAlO3]-0.01NaNbO3 ferroelectric ceramics under shock wave compression. A current profile with a maximum value of ∼25 A and a FWHM of ∼2.3 μs was obtained. Particularly, the poled BNT-BA-0.01NN ceramics were almost completely depolarized under high strain rate loading, releasing a high charge density J of 38 μC/cm2. The released J was approximately 96% of thermal-induced charge density (∼40 μC/cm2), which was 18% higher than that of PZT95/5 ceramics. The shock-induced depolarization mechanism can be attributed to the ferroelectric-ergodic relaxor phase transit...