금속 착물을 함유한 폴리술폰 지지층을 이용한 폴리아미드계 복합막의 제조 및 정삼투 성능 평가
2016
Thin film composite (TFC) polyamide membranes were prepared on polysulfone (PSF) supports for forward osmosis (FO) applications. To understand the influence of polarity and porosity of support layer on the formation of polyamide structure and the final FO performance, clathochelate metal complex (MC) contained PSF supports were prepared via the phase inversion process from various PSF casting solutions containing 0.1-0.5 wt% of MC in dimethyl formamide (DMF) solvent (18 wt%). A crosslinked aromatic polyamide layer was then fabricated on top of each support to form a TFC membrane. For the porous PSF supports prepared with relatively low concentration casting solutions (12 wt%), the PET film was removed after phase inversion and crosslinked aromatic polyamide layer was then fabricated. The tested sample from PSF (18 wt%)/MC (0.5 wt%) casting solution presented outstanding FO performance, almost similar water flux (9.99 LMH) with lower reverse salt flux (RSF, 0.77 GMH) compared to commercial HTI FO membrane(10.97 LMH of flux and 2.2 GMH of RSF). By addition of MC in casting solution, the thickness of the active layer in FO membranes was reduced, however, the increased RSF value was obtained.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
0
References
0
Citations
NaN
KQI