Influence of annealing temperature on structural and optical properties of Lu{sub 2}O{sub 3}:Eu{sup 3+}, Tb{sup 3+} transparent films

Highlights: • Lu{sub 2}O{sub 3}:Eu{sup 3+}, Tb{sup 3+} films were synthesized by sol–gel and by dip-coating technique. • Effects of annealing treatment on structural and optical properties were studied. • Optogeometrical characteristics of synthesized films were analyzed. • X-ray diffraction results showed that Lu{sub 2}O{sub 3}:Eu{sup 3+}, Tb{sup 3+} crystallizes at 700 °C. • High reddish emission on transparent films with at least 1 μm thick was observed. - Abstract: High-optical quality Lu{sub 2}O{sub 3}:Eu{sup 3+} 5 mol%, X Tb{sup 3+} (X = 0–0.04 mol%) thin films were prepared by the sol–gel process and dip-coating technique. The procedure was as follows: lutetium, europium and terbium nitrates were used as precursors, and ethanol as a solvent. Etylenglycol (EG) was added as a sol stabilizer, and the pH was adjusted by acetic acid. After 10 dipping-cycles, followed by an annealing process (600–900 °C) for 1 h, transparent, smooth and crack-free films (ra = 8–9 nm) were formed. The X-ray diffraction (XRD) results showed crystallized films into the cubic structure at 800 °C. The ellipsometry results showed that the thickness of the films varied from 1 to 1.4 μm at 1000 and 600 °C, respectively. Finally, the films presented a typical Eu{sup 3+}more » red emission at 611 nm ({sup 5}D{sub 0} → {sup 7}F{sub 2}); furthermore, the effect of the Tb{sup 3+} content showed that the highest emission intensity corresponded to the lower Tb{sup 3+} content.« less