Effects of density on the mechanical properties of spark plasma sintered β-SiC

Abstract The influence of density on the hardness value of β-SiC samples was studied based on Knoop and Vickers indentation tests. Hardness measurements were performed on additive-free spark plasma sintered SiC samples in the [80%–95%] density range and on highly dense samples (>99%) sintered with very low content of sintering aids. Results revealed that the density has a strong influence on the hardness value, which increases of about 7 GPa between samples presenting densities of 80% and 95% and even reaches 21 GPa under 2 kg with Knoop indenter for the densest samples sintered with very low content of sintering aids. These results allowed us to give a comprehensive model-supported analysis of the mechanical properties of spark plasma sintered β-SiC with controlled porosity that currently does not exist in the literature. The calculation of Young modulus and toughness further resulted in encouraging properties for our samples with regards to mechanical and ballistic performances.