Infrared properties of β-sialon as a function of composition

Abstract The infrared properties of β -sialons, Si 6− z Al z O z N 8− z , prepared by hot, isostatic pressing for nine z -values, as well as a corresponding set of samples containing 1 wt% of yttria have been studied. The samples all have densities over 99% of their theoretical value and were found to be single-phased for z β -Si 3 N 4 sample were used for infrared reflectance measurements. The lattice bands in the infrared reflectance spectra were analyzed for the different compositions. Numerical fits, using the parameters for a maximum of five classical Lorentz oscillators as free variables, were carried out. A strong Si–N resonance at 900 cm −1 was identified, the oscillator strength of which scaled linearly with z . The IR reflectance bands represent a potential for selectively low emittance applications on radomes in the 8–12 μ m atmospheric window. The evaluation of the appropriate average window emittance showed a close to linear increase from about 0.5 to 0.9 for 0.35 z