Materiais compósitos a base de PP e Muscovita

EnglishComposites based on polypropylene (PP) and muscovite mica in concentrations varying from 0–20% were obtained via extrusion. The muscovite in natura was processed and after characterization by diffraction X–ray and SEM revealed no alterations in the crystalline structure and maintenance of the lamellar structure. The composites of PP/mica showed a reduced melt index and a progressive increase in the value of the density and hardness of the material. In thermal analysis (TG / DSC) there was slight increase in the decomposition temperature of the Polypropylene in the composites containing 10, 15, and 20% mica. The analysis of the mechanical properties by tensile tests revealed slight increase in the Young's Modulus (610 MPa in pure PP to 750 Mpa in PP/20%mica) attributed to restricted mobility of the polymer chains imposed by the presence of mica. portuguesCompositos com base em polipropileno (PP) e mica do tipo muscovita em concentracoes variando de 0–20% foram obtidos via extrusao. A muscovita in natura foi beneficiada e caracterizada por difracao de raios–X e MEV que revelaram a ausencia de alteracoes na estrutura cristalina e manutencao da estrutura lamelar. Os compositos de PP/mica obtidos apresentaram reducao no indice de fluidez e um aumento progressivo no valor da densidade e na dureza do material. Nas analises termicas (TG/DSC) verificou–se ligeiro aumento da temperatura de decomposicao deslocamento do PP para os compositos com 10, 15 e 20% de mica. A analise das propriedades mecânicas por meio de ensaios de tracao, revelou ligeiro aumento no modulo de Young, (de 610 Mpa no PP puro para 750 Mpa no PP/20%mica) atribuido a restricao da mobilidade das cadeias imposta pela presenca da mica.