INTERCORRELATION OF SURFACE FREE ENERGY AND ANODE CAPACITY OF ALUMNIUM ALLOY ANODES

Surface free energies have been evaluated from Young’s moduli and lattice parameter data of five aluminium alloys with varying amounts of stanum to determine the inter-correlation with anode capacity of the alloys. The composition containing ~1.47%Sn exhibits a minimum in the surface free energy which accounts for the decrease in the tendency of the alloy to undergo passivation thus resulting in a higher anode capacity of 2478Ah/kg at ≈ 0.08mA/cm 2 , current density. The results showed that aluminium alloy containing certain amount of stanum has lowered surface free energy, leading to reduction in passive film thickness and reduces metal/oxide bond strength. These factors in turn result in a better cathodic protection property of aluminium alloy containing stanum. ABSTRAK Tenaga bebas permukaan yang telah dihitung daripada data modulus Young dan parameter kekisi bagi lima aloi aluminium yang mengandungi pelbagai kandungan stanum bagi menentukan saling kolerasinya dengan kapasiti anod aloi yang dikaji. Aloi yang mengandungi ~1.47%Sn menunjukkan nilai tenaga bebas permukaan terendah yang mendorong kepada pengurangan kecenderungan aloi untuk menjadi pasif dan seterusnya menyebabkan kapasit anod menjadi lebih tinggi iaitu 2478Aj/kg pada ketumpatan arus ≈ 0.08mA/cm 2 . Keputusan ini menunjukkan bahawa aloi yang mengandungi sejumlah tertentu stanum dapat merendahkan nilai tenaga bebas permukaan, yang mampu mengurangkan ketebalan filem pasif dan kekuatan ikatan logam dengan oksida. Faktor-faktor ini menghasilkan sifat perlindungan katod yang baik bagi aloi aluminium yang mengandungi stanum.