Effect of isothermal heat treatment on microstructure and mechanical properties of Reduced Activation Ferritic Martensitic steel

Abstract Hardness, tensile properties and microstructural changes in 9Cr–1W–0.06Ta–0.22V–0.08C Reduced Activation Ferritic–Martensitic steel have been investigated after subjecting the steel with isothermal heat treatments for 5 min at temperatures in the range 973–1473 K (below Ac 1 to above Ac 3 transformation temperatures) followed by oil quenching and tempering at 1033 K for 1 h. These studies have been carried out in an effort to assess the strength of the steel at different microstructural conditions. Optical, scanning and transmission electron microscopic investigations have been carried out to assess the microstructural changes of the steel upon various heat treatments. The steel developed predominantly tempered martensitic structure after the heat treatments. The hardness, tensile strength and the prior austenitic grain size of the steel exhibited minimum values for soaking heat treatment in the intercritical temperature range (i.e.) between Ac 1 and Ac 3 ; whereas the ductility was maximum. With increase in isothermal heat treatment temperature above Ac 3 , hardness, tensile strength and grain size of the steel were found to increase with consequent decrease in tensile ductility. TEM investigations revealed that the coarsening of subgrain and precipitates at grain and sub-grain boundaries on heat treatment of the steel in the inter-critical temperature range. The tensile properties of the steel have been correlated with microstructure.