YDyxBa2Cu3O7-δ Epitaxial Films Prepared by Chemical Solution Deposition

YBa2Cu3O7-δ (YBCO) coated conductors have wide-ranging potential in large scale applications, such as, superconducting maglev trains and superconducting electric cables, but low current carrying capability restrains the practical application of YBCO coated conductors at high temperatures and high magnetic fields. It is crucial to develop YBCO coated conductors with high flux pinning capability. In this paper, epitaxial, dense, smooth and crack-free YDyxBa2Cu3O7-δ (x = 0~0.5) films were prepared on a LaAlO3 (LAO) single crystal substrate via a fluorine-free polymer-assisted metal organic deposition (PA-MOD) method. The effects of Dy addition on the microstructure and superconducting character of YBCO films were investigated. The all films show a strong c-axis orientation and good texture in-plane and out of plane. The Dy addition to the YBCO film hardly affects the critical temperature of YBCO superconductor. The irreversibility fields of YBCO films can be improved with the Dy addition x = 0.5 compared to the pure YBCO film but decreased in the x = 0.3 sample.