Field electron extraction from surface modified Cd(OH)2 nanowires

The Cd(OH)2 nanowires were grown on Silicon(Si) substrate by simple chemical bath deposition technique and gold(Au) nanoparticles were decorated on surface of the Cd(OH)2 nanowiresby sputtering method. Detail characterization such as morphological and structural analysis of Au/Cd(OH)2 nanowires has been carried out using Field Emission Scanning Electron Microscope and X-ray Diffraction. Low turn-on field of 0.75 V/μm was found forthe emission current density of 10 µA/cm2 and high currentdensity of 1.478mA/cm2 was drawn at an applied field of 1.6 V/μm from Au/Cd(OH)2 nanowires, observed low turn-on field was found superior to other metal nanoparticles decorated semiconducting nanostructures reported in the literature. Also the field emission current stability for the preset value of 10 µA over the period of 3 hr is found to be good. To the best of our knowledge, this is the first report on the synthesis and field emission studies Au/Cd(OH)2 nanowires.