Macadamia nut shell-derived carbon composites for post combustion CO2 capture

Abstract A great interest has been devoted, in recent years, to development of novel cost-effective and environmentally friendly technologies to make CO 2 capture economically viable. Compared with other available technologies, solid adsorbent capture technologies have the potential to be highly cost-effective and could have less impact on the environment. In this paper, new carbon composites were developed with macadamia nut shells (MNSs), phenolic resin and carbon fibers as solid adsorbents for post combustion capture (PCC) of CO 2 from coal-fired power stations. Many have claimed the superiority of their adsorbents in terms of the capture capacities at atmospheric pressure (760 mmHg). However, for CO 2 adsorption capacities at PCC conditions (typically about 10–15% in Australia), the CO 2 partial pressure should be considered. Thus, here we introduced a new term, C 100 as an indicator of CO 2 capture performance of solid adsorbents at 298 K and 100 mmHg. Compared to our previous carbon fiber adsorbent ( Thiruvenkatachari et al., 2009 ), new composites were found to possess about maximum 35% higher C 100 . Also, in this paper, we stressed the importance of MPSDs (ranging from 4 to 6 A) of solid adsorbents as they are directly associated with CO 2 capture performance of adsorbents at PCC conditions. When mixed with phenolic resin, carbonized MNSs yielded higher C 100 than activated ones, indicating that the volatile matter in MNSs contributed to creation of small pores during the composite fabrication process. It was observed that the same held for carbon fibers. The MPSDs were used to explain carbonization and activation processes of MNS-derived carbons, phenolic resin, carbon fibers and their composites. A diffusional problem of CO 2 molecules was identified for carbonized phenolic resin (glass carbon structure) and explained with its MPSDs. When phenolic resin is mixed with MNS-derived carbons and carbon fibers in composite forms, there was no pore accessibility problem of CO 2 observed for all the composites synthesized in this paper. This paper provides useful pore structural information relevant to CO 2 capture at PCC conditions to those who are dealing with solid sorbents.