20 T Compact Superconducting Outsert Employing Y123 Coated Conductors for a 45 T Hybrid Magnet

2009 
We have been developing high-strength Nb 3 Sn strand cables to construct a high-field superconducting outsert for a 45 T hybrid magnet with a 25 T water-cooled resistive magnet. Evidence for cold work strengthening of repeated bending treatment (prebending effect) on Nb 3 Sn strands internally reinforced with CuNb stabilizer, which exhibits significant enhancement of the critical current density, has been found in the superconducting magnet fabrication process using a react-and-wind method. The strand cables were designed by controlling the constituent number of CuNb/Nb 3 Sn strands with the prebending effect and stainless steel strands, which are expected to have a stress limit 580 MPa at 0.4% strain. In order to design a compact superconducting outsert, high-strength strand cables are adopted in a magnetic field region below 14 T to maintain relatively large engineering current densities (J e ). In a higher-field region above 14 T, YBa 2 Cu 3 O 7 (Y123) coated conductors are employed for an insert coil. Using combination of Y123, Nb 3 Sn and NbTi superconductors, a 20 T superconducting outsert with a room temperature bore of 400 mm consisting of three layers made of Y123, two layers of CuNb/Nb 3 Sn and two layers of NbTi was designed. The coil parameters are 440 mm inner diameter, 1080 mm outer diameter and 1138 mm coil height. A very compact 20 T superconducting outsert with a stored magnetic energy 72 MJ at an operation current 903 A can be developed for a 45 T hybrid magnet.
    • Correction
    • Source
    • Cite
    • Save
    • Machine Reading By IdeaReader
    10
    References
    12
    Citations
    NaN
    KQI
    []