Microstructure and mechanical properties of hot extruded Mg–Al–Mn–Ca alloy produced by rapid solidification powder metallurgy

Abstract The microstructure and mechanical properties of hot extruded Mg–Al–Mn–Ca alloy was investigated. Both rapid solidified powders and cast billets were extruded at 573, 623 and 673 K to optimize the processing conditions for obtaining better mechanical response. Powder was consolidated to prepare the extrusion billets using both cold compaction and Spark Plasma Sintering at 473 K. The tensile properties of the extruded alloy were then evaluated and correlated to the observed microstructure. The results show that the use of rapid solidified powder could lead to effective grain refinement, which in turn resulted in the improved mechanical response, especially compared to the extruded conventional cast material.