Structural comparison of GdF_3 films grown on CaF_2 (111) and SiO_2 substrates
2008
Wide bandgap metal fluorides are the materials of choice for optical coating applications at 193 nm. Low loss and environmentally stable optics requires a mitigating fluoride film structure on a nanometer scale. To understand the growth mechanism of fluoride materials, GdF3 films grown on CaF2 (111) and SiO2 substrates were investigated. Film inhomogeneity and surface roughness were modeled by fitting ellipsometric data with an effective medium approximation, indicating a correlation between film inhomogeneity and surface roughness. The modeled surface roughness was compared with the atomic force microscope measurement. Film inhomogeneity was correlated to the cone-shaped columnar structure revealed by cross-sectional images from a scanning electron microscope. The film crystalline structure was determined by x-ray diffraction measurement, suggesting a different growth mechanism of GdF3 films on crystalline and amorphous substrates.
Keywords:
- Correction
- Cite
- Save
- Machine Reading By IdeaReader
8
References
0
Citations
NaN
KQI