Analysis of the osteogenic and mechanical characteristics of iron (Fe2+/Fe3+)-doped β‑calcium pyrophosphate

Abstract The calcium phosphate is the main mineral constituent of bone. Although there has been significant amount of research on finding ideal synthetic bone, no suitable scaffold material has yet been found. In this investigation, the iron doped brushite (CaHPO4·2H2O) has been investigated for osteogenic potential and mechanical properties. The synthesis of iron-oxide doping in the form of Fe2+,3+-ions were carried out using the solution based method in which the ammonium hydrogen phosphate and calcium nitrate solutions were used in stoichiometric ratio for synthesizing CaHPO4·2H2O, with doping concentrations of Fe2+,3+-ions between 5 mol% and 30 mol%. The synthesized powders were analysed using X-ray powder diffraction, FTIR, SEM and Raman spectroscopic techniques. The heat treatment of synthesized powder was carried out at 1000 °C in air for 5 h, and it was found that the dominant crystalline phase in samples with