Fatigue Behavior of A Minor Yttrium Doped ZrCuNi-Based Metallic Glass Alloy Fabricated by Industrial Grade Raw Material

The fatigue behavior of a low-cost Zr52.1Ti5Cu17.9Ni14.6Al10Y0.4 (at%) (ZrCuNi-based) bulk-metallic glass (BMG) prepared by industrial-grade material was investigated under three-point bending loading modes. In order to obtain the fatigue stress-life (S-N) data, stress-controlled experiments were conducted using a computer-controlled material test system electrohydraulic testing machine at 60 Hz with a 0.1 R ratio in the air at room temperature. The fatigue limit (~174 MPa) in stress amplitude and fatigue ratio (~0.14) of this BMG is comparative to the similar BMG (Vit-105) prepared by high pure raw materials. The crack initiated from inclusions near the rectangular corners at the outer surface of the rectangular beam due to stress concentration. The striations and vein-like patterns were observed in the crack propagation region and fast fracture region, respectively.