Influence of heating rate on the crystalline properties of 0.7BiFeO3–0.3PbTiO3 thin films prepared by sol–gel process

Abstract 0.7BiFeO 3 –0.3PbTiO 3 (BFPT7030) thin films were deposited on SiO 2 /Si substrates by sol–gel process. The influence of heating rate on the crystalline properties of BFPT7030 thin films were studied by X-ray diffraction (XRD), scanning electron microscope (SEM), atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). XRD patterns of the films showed that a pure perovskite phase exists in BFPT7030 films annealed by rapid thermal annealing (RTA) technique. SEM and AFM observations demonstrated that the BFPT7030 films annealed by RTA at 700 °C for 90 s with the heating rate of 1 °C s −1 could show a dense, crack-free surface morphology, and the films’ grains grow better than those of the films annealed by RTA at the same temperature with other heating rates. XPS results of the films indicated that the ratio of Fe 3+ :Fe 2+ is about 21:10 and 9:5 for the films annealed by RTA at 700 °C for 90 s with the heating rate of 1 and 20 °C s −1 , respectively. That means the higher the heating rate, the higher the concentration of Fe 2+ in the BFPT7030 thin films.