High‐efficiency black silicon interdigitated back contacted solar cells on p‐type and n‐type c‐Si substrates
2015
This work demonstrates the high potential of Al2O3 passivated black silicon in high-efficiency interdigitated back contacted
(IBC) solar cells by reducing surface reflectance without jeopardizing surface passivation. Very low reflectance values, below
0.7% in the 300–1000 nm wavelength range, together with striking surface recombination velocities values of 17 and
5 cm/s on p-type and n-type crystalline silicon substrates, respectively, are reached. The simultaneous fulfillment of requirements,
low reflectance and low surface recombination, paves the way for the fabrication of high-efficiency IBC Si solar
cells using black silicon at their front surface. Outstanding photovoltaic efficiencies over 22% have been achieved both
in p-type and n-type 9-cm2 cells. 3D simulations suggest that efficiencies of up to 24% can be obtained in the future with
minor modifications in the baseline fabrication process.