Magnetic and elastic properties of CoFe2O4- polydimethylsiloxane magnetically oriented elastomer nanocomposites

Magnetic elastic structured composites were prepared by using CoFe2O4 ferromagnetic and superparamagnetic nanoparticles as fillers in polydimethylsiloxane (PDMS) matrixes, which were cured in the presence of a uniform magnetic field. Cobalt-iron oxide nanoparticles of three different average sizes (between 2 and 12 nm) were synthesized and characterized. The smallest nanoparticles presented superparamagnetic behavior, with a blocking temperature of approximately 75 K, while larger particles are already blocked at room temperature. Macroscopically structured-anisotropic PDMS-CoFe2O4 composites were obtained when curing the dispersion of the nanoparticles in the presence of a uniform magnetic field (0.3 T). The formation of the particle’s chains (needles) orientated in the direction of the magnetic field was observed only when loading with the larger magnetically blocked nanoparticles. The SEM images show that the needles are formed by groups of nanoparticles which retain their original average size. The Yo...