Electron microscopy analyses and electrical properties of the layered Bi2WO6 phase

Abstract The bismuth tungstate Bi 2 WO 6 was synthesized using a classical coprecipitation method followed by a calcination process at different temperatures. The samples were characterized by X-ray diffraction, simultaneous thermogravimetry and differential thermal analysis (TGA/DTA), scanning and transmission electron microscopy (SEM, TEM) analyses. The Rietveld analysis and electron diffraction clearly confirmed the Pca 2 1 non centrosymmetric space group previously proposed for this phase. The layers Bi 2 O 2 2+ and WO 4 2− have been directly evidenced from the HRTEM images. The electrical properties of Bi 2 WO 6 compacted pellets systems were determined from electrical impedance spectrometry (EIS) and direct current (DC) analyses, under air and argon, between 350 and 700 °C. The direct current analyses showed that the conduction observed from EIS analyses was mainly ionic in this temperature range, with a small electronic contribution. Electrical change above the transition temperature of 660 °C is observed under air and argon atmospheres. The strong conductivity increase observed under argon is interpreted in terms of formation of additional oxygen vacancies coupled with electron conduction.