The influence of non-magnetic particles on the coercive force and the initial susceptibility

In a ferromagnetic alloy the dependence of the coercive force HC and the initial susceptibility χa on the size and the number of non-magnetic inclusions has been experimentally investigated. Cylindrical single crystals with their rod axis parallel to the magnetic soft direction have been used as specimens. The material PE 16 is a commercial Ni-based alloy which by suitable heat treatment precipitates spherical, non-magnetic particles of Ni3(Al, Ti), which do not strain the matrix. The dependence of HC and χa on the particle diameter d is in agreement with theoretical predictions. The relation between these two parameters and the volume fraction v cannot be described by the corresponding equations. This discrepancy is probably due to the fact that the Bloch-Wall geometry within the specimen does not remain constant with varying v. The product HC · χa has been found independent of v and d. An einer ferromagnetischen Legierung wurde die Abhangigkeit der Koerzitivfeldstarke HC und der Anfangssuszeptibilitat χa von der Grose und Anzahl nichtmagnetischer Ausscheidungen experimentell untersucht. Es wurden zylindrische Einkristalle verwandt, deren Stabachse in die magnetisch weiche Richtung orientiert war. Ausgangsmaterial war die auf Ni basierende Legierung PE 16, die bei geeigneter Warmebehandlung kugelformige, nicht-magnetische Teilchen der Zusammensetzung Ni3(Al, Ti) ausscheidet. Die Teilchen verspannen die Matrix nicht. Die gemessene Abhangigkeit von HC und χa vom Teilchendurchmesser d ist in Ubereinstimmung mit theoretischen Beziehungen. Ein entsprechender Zusammenhang zwischen diesen beiden Grosen und dem ausgeschiedenen Volumenbruchteil v konnte nicht bestatigt werden. Vermutlich andert sich mit v auch die Blochwand-Geometrie innerhalb der Probe. Das Produkt HC · χa ist unabhangig von v und d.