Effect of heat treatment and bend strain on the Jc of Ag-sheathed Bi-2212 tape

Bi-2212 tapes were fabricated using a powder-in-tube method and their superconducting properties were measured as a function of heat treatment. The tapes were heated to temperature, T1 (884-915 °C), and kept at that temperature for 20 min to induce partial (incongruent) melting. The samples were cooled to T2 with a ramp rate of 120 °C h-1 and then slowly cooled to T3 with a cooling rate, R2, and from T3 to T4 with a cooling rate, R3. The tapes were kept at the temperature T4 for P1 hours and then cooled to room temperature. Both R1 and R2 were chosen between 2 and 8 °C h-1. It was found that the structure and Jc of the tapes depend on the sintering conditions, i.e. T1-4, R1-3 and P1. The highest Jc of 5800 A cm-2 was obtained at 77 K in a self-field with heat treatment where T1 = 894 and 899 °C, R1 = R2 = 5 °C h-1 and P1 = 6 h were employed. When 0.7% of bend strain, which is equivalent to a bend radius of 5 mm, was applied to the tape, 80% of the initial Jc was sustained.