Flood Mud as Geopolymer Precursor Materials: Effect of Curing Regime on Compressive Strength

This paper studies the effect of curing temperature and curing duration to the flood mud based geopolymer on compressive strength properties. Flood mud was used as a raw material for geopolymer and geopolymer samples were synthesized by using sodium silicate and sodium hydroxide 14M solution. These samples were cured at different temperature (100°C, 150°C, 200°C and 250°) for different curing duration (6h, 12h and 24h) respectively. Compressive strength tests were carried out at after 28 days. The compressive strength and SEM analysis of geopolymer products were evaluated. Result showed that the maximum compressive strength was 24 MPa at temperature of 150°C for 24 hours. With increasing ageing day, densification of geopolymer gel was observed.