True Photoreactivity Origin of Ti 3+ -DopedAnatase TiO 2 Crystals with Respectively Dominated Exposed{001}, {101}, and {100} Facets

Combining the advantages of reactive crystal facets and engineering defects is an encouraging way to address the inherent disadvantages of titanium dioxide (TiO2) nanocrystals. However, revealing the true photoreactivity origin for defective TiO2 with coexposed or predominant exposed anisotropic facets is still highly challenging. Here, the photoreactivity of TiO2 nanocrystals with respectively predominant exposed {001}, {101}, and {100} facets before and after Ti3+ doping under both ultraviolet and visible light was compared systematically. In detail, the photocatalytic H2 production for R-TiO2-001, R-TiO2-101, and R-TiO2-100 increased by a factor of 1.34, 2.65, and 3.39 under UV light and a factor of 8.90, 13.47, and 8.72 under visible light. By contrast, the photocatalytic degradation of methyl orange for R-TiO2-001, R-TiO2-101, and R-TiO2-100 increased by a factor of 3.18, 1.42, and 2.17 under UV light and a factor of 4.03, 2.85, and 1.58 under visible light, respectively. The true photocatalytic acti...