Experimental Investigation of Porosity Formation During the Slow Injection Phase in High-Pressure Die-Casting Processes

The air entrapment mechanisms in die-casting injection chambers that may produce porosity in manufactured parts are analyzed in this work using visualization techniques of the flow in a transparent injection chamber model, using water as working fluid. In particular, results for the free-surface profile evolution and for the volume of air remain-ing in the chamber at the instant at which the water begins to flow through the runner are analyzed for different maximum plunger speeds and initial filling fractions. A comparison between these visualizations and the numerical results of Zamora et al. (2007, "Experimental Verification of Numerical Predictions for the Optimum Plunger Speed in the Slow-Phase of a High-Pressure Die Casting Machine," Int. J. Adv. Manuf. Technol., 33, pp. 266-276) which were obtained using a three-dimensional numerical model, shows a good degree of agreement. After discussing the air entrapment mechanisms that may produce porosity in manufactured parts, different experiments, which were carried out under real operating conditions using an aluminum alloy in a high-pressure die-casting machine with horizontal cold chamber, will be presented. The die-cavity geometry used in the experiments was appropriately modified to isolate the slow shot phase from the rest of the injection process, and the porosity levels in the manufactured parts were measured using a gravimetrie technique. The optimum values of the maximum plunger speed that minimizes porosity in the manufactured parts have been determined. These values are very close to the previous numerical predictions of Lopez et al. (2003, "On the Critical Plunger Speed and Three-Dimensional Effects in High-Pressure Die Casting Injection Chambers, " ASME J. Manuf. Sci. Eng., 125, pp. 529-537).