Thermal properties and crystalline structure of liquid crystalline poly(ethylene terephthalate‐co‐2(3)‐chloro‐1,4‐phenylene terephthalate)

Thermal properties and crystalline structure of liquid crystalline (LC) poly(ethylene terephthalate-co-2(3)-chloro-1,4-phenylene terephthalate) [copoly(ET/CPT)] were investigated using differential scanning calorimetry (DSC), thermogravimetry (TGA), limiting oxygen index (LOI) measurement, electron dispersive X-ray analysis (EDX), X-ray diffractometry, and infrared spectrometry (IR). The thermal transition temperatures of copoly(ET/CPT) were changed with the composition. Copoly(ET/CPT) showed two thermal decomposition steps and the residues at 700°C and LOI values of copoly(ET/CPT) were almost proportional to its chlorine content. The activation energy of thermal decomposition of LC units was very low compared to that of poly(ethylene terephthalate)(PET) units. Crystal structure of copoly(ET/CPT) (20/80) was of triclinic system with the lattice constants of a = 9.98 A˚, b = 8.78 A˚, c = 12.93 A˚, α = 97.4°, β = 96.1°, and γ = 90.8°, which is very close to that of poly(chloro-p-phenylene terephthlate) (PCPT) with the lattice constants of a = 9.51 A˚, b = 8.61 A˚, c = 12.73 A˚, α = 96.8°, β = 95.4°, and γ = 90.8°. When copoly(ET/CPT)(50/50) was annealed at 220°C in vacuum, crystallization induced sequential reordering (CISR) was not observed but the heat of fusion was slightly increased due to the increase of the trans isomer content in PET units. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 1286–1294, 2002; DOI 10.1002/app.10451