Development of fiber-reinforced polypropylene with NaOH pretreated rice and coffee husks as fillers: Mechanical and thermal properties

Incorporation of agricultural wastes as fillers in fiber-reinforced plastics is gaining momentum in plastics engineering research. In this study, fiber-reinforced polypropylene (PP) with rice and coffee husks as filler material were developed. The effect of alkali (sodium hydroxide) pretreatment of the husks on mechanical and thermal properties of developed PP biocomposites was observed. Filler material loading was varied from 0% to 20% for rice husks and 0% to 10% for coffee husks. A twin-screw extruder was used for compounding the PP matrix with rice and coffee husk filler materials. Tensile strengths and percentage elongation results varied from 27.4 to 37.4 MPa and 2.4% to 70.3% (unmodified coffee husks), 31.1 to 37.4 MPa and 5% to 70.3% (unmodified rice husks), 30.7 to 37.4 MPa and 5.3% to 70.3% (modified coffee husks), and 30.7 to 37.4 MPa and 4.8% to 70.3% (modified rice husks). Young’s modulus ranged between 1656 and 2247.8 MPa for biocomposite PP samples with unmodified filler material. Young’s m...