The dynamic mechanical behaviour of blends of polyphenylene sulfide with acetylene terminated sulfone

The dynamic mechanical behaviour of blends of poly(phenylene sulfide) (PPS) with the acetylene terminated sulfone bis(4-(4-ethynylphenoxy)phenyl)sulfone (ESF) was investigated by torsional braid analysis (TBA). A uniform dispersed system of ESF/PPS may be obtained by a solution process at 200°C, and can be maintained during the heat treatment up to 400°C. The increase of Tg of the blended system was found to be inappreciable by one-step and short time (e.g. 1 h) heat treatment, whatever the ESF fraction is. By a long term heat treatment or by step-curing, the Tg of the system may be raised from 180 to 220°C, in company with the increase of rigidity at 300°C, compared with pure PPS. The flexural modulus and interlaminar shear strength of continuous unidirectional carbon fibre composites with a blended matrix of ESF/PPS = 10/90 are significantly higher than those of composites with pure PPS matrix. An einem mit Blends von Polyphenylensulfid (PPS) und einem acetylenterminierten Sulfon Bis(4-(4-ethinylphenoxy)phenyl)sulfon (ESF) impragnierten Kohlenstoff-Faser-Band wurde eine Torsionsanalyse zur Bestimmung des dynamisch-mechanischen Verhaltens durchgefuhrt. Ein gleichmasig disperses System kann durch einen Losungsprozes bei 200°C erzielt und wahrend der Hitzebehandlung bis zu 400°C aufrecht erhalten werden. Ein Anstieg von Tg bei den legierten Systemen war bei einer Einstufen-Kurzzeit-Erhitzung (1 h) kaum feststellbar, unabhangig von der Art der ESF-Komponente. Durch langes Erhitzen oder durch stufenweise Hitzebehandlung kann Tg von 180 bis 220°C anwachsen, parallel zu einem Anstieg der Steifigkeit bis 300°C gegenuber reinem PPS. Der Biegemodul und die interlaminare Scherfestigkeit eines kontinuierlich einachsig gerichteten Kohlenstoff-Faser-Verbundstoffs mit einer Matrix aus 10/90 ESF/PPS-Legierung sind signifikant hoher als bei einer reinen PPS Matrix.