Pre-and post-irradiation deformation effects on thermoluminescence studies in barium-doped NaCl crystals
1984
Glow curves are recorded for NaCl:Be specimens subjected to pre-irradiation thermal quenching and post-irradiation plastic deformation. These specimens are irradiated by X-rays. Three glow peaks are observed around 65, 140, and 195 °C in virgin crystals on pre-irradiation thermal quenching and post-irradiation plastic deformation results in an additional glow peak in the region 240 to 250 °C. It is suggested that vacancy clusters and dislocation dipoles produced during deformation influence the thermoluminescence process of the pre-treated and post-treated samples.
Die Glowkurven fur NaCl:Ba-Proben, die vor Bestrahlung thermisch abgeschreckt und nach Bestrahlung plastisch deformiert werden, werden aufgezeichnet. Drei Glow-Maxima werden in jungfraulichen Kristallen bei 65, 140 und 195 °C nach thermischer Abschreckung vor der Bestrahlung beobachtet und plastische Deformation nach Bestrahlung fuhrt zu einem zusatzlichen Glowmaximum im Bereich von 240 bis 250 °C. Es wird angenommen, das Leerstellencluster und Versetzungs-dipole, die wahrend der Deformation erzeugt werden, den Thermolumineszenaprozes der vorund nachbehandelten Proben beeinflussen.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
9
References
2
Citations
NaN
KQI