Spectrally-broadened multimode lasing based on structurally graded InGaN nanocolumn photonic crystals suitable for reduction of speckle contrast

Bottom-up grown structurally graded InGaN-based nanocolumn photonic crystals, in which nanocolumns were arranged in triangular lattice and the nanocolumn diameter changed one-dimensionally from 93 to 213 nm with a fixed lattice constant of 250 nm, were fabricated. The spatial distribution of the diameter resulted in random-laser-like operation under optical excitation. A broad multi-wavelength lasing spectrum with more than 10 peaks was obtained with a full width at half maximum of 27 nm at 505 nm wavelength as well as lowering of the polarization degree, which is expected to be suitable for speckle contrast reduction in laser projection display applications.