Boron-assisted transformation to rod-like graphitic carbons from multi-walled carbon nanotubes in boron-mixed multi-walled carbon nanotube solids.

We produced boron-mixed multi-walled carbon nanotube solids (B-mixed MWCNT solids) by heating and pressing the powder of purified MWCNTs mixed with 1, 5, and 10 wt % boron in the temperature range 1400–1800 °C every 200 °C under a constant pressure of 20 MPa in vacuo, and investigated the influence of boron addition on nanotube structure and the mechanical and electrical properties of the resulting B-mixed MWCNT solids. The structure of the prepared material was characterized by scanning electron microscopy equipped with energy-dispersive X-ray spectroscopy, high-resolution transmission electron microscopy-electron energy loss spectroscopy, Raman scattering spectroscopy, and X-ray diffraction, and their mechanical properties and conductivity were measured using a mechanical and Vickers indentation tester and an electric resistor, respectively. It is notable that part of the nanotubes in the B-mixed MWCNT solids solidified at 1800 °C had dramatically changed into rod-like graphitic carbons (RLGCs). The occ...