Hydrogen storage properties of Mg–Ni–C system hydrogen storage materials prepared by hydriding combustion synthesis and mechanical milling

Abstract Mg–Ni–C composite hydrogen storage materials were prepared by first ball milling the powder mixtures of carbon aerogel and nano-Ni, and then mixed with magnesium powder followed by hydriding combustion synthesis (HCS). The HCS product was further treated by mechanical milling for 10 h. The effect of Ni/C ratio on the structures and hydrogen absorption/desorption properties of the materials were studied by means of X-ray diffraction (XRD), scanning electron microscopy (SEM) and pressure–composition–temperature (PCT) measurements. It is found that 90Mg–6Ni–4C system shows the best hydriding/dehydriding properties, which absorbs hydrogen at a saturated capacity of 5.23 wt.% within 68 s at 373 K and desorbs 3.74 wt.% hydrogen within 1800 s at 523 K. Moreover, the dehydriding onset temperature of the system is 430 K, which is 45 K lower than that of 90Mg–10Ni system or 95 K lower than that of 90Mg–10C system. The improved hydriding/dehydriding properties are related greatly to the Ni/C ratio and the structures of the composite systems.