A million-microchannel multifuel steam reformer for hydrogen production

Abstract A functionalized silicon micromonolith of 7 mm in diameter and 210 µm-thick was evaluated for the production of hydrogen from the steam reforming (SR) of various fuels, containing different functional groups, such as ethanol, acetic acid, 2-propanol, acetone, and 2-methoxyethanol. The micromonolith consisted of 2 million regular channels of 3.3 µm in diameter, which were coated with a 100-nm RhPd/CeO2 catalytic layer. The catalytic activity was tested at temperatures between 823-1023 K, using overstoichiometric steam-to-carbon ratios and operating at contact times between 0.005-0.009 s. The best performance was obtained for the 2-methoxyethanol SR tests, where 53% H2 selectivity was recorded. A remarkable hydrogen production normalized by reactor volume of 110 LNH2·mL2-methoxyethanol,liquid-1 cm-3Reactor was recorded, leading to comparable H2 yields to those obtained with a conventional monolith coated with the same RhPd/CeO2 catalyst, owing to the large contact area. After more than 80 hours under reaction conditions, the micromonolith was characterized by SEM and TEM. SEM analyses showed that no channels were blocked due to carbon deposition nor detached CeO2 layers were found. These results demonstrate the feasibility of using catalytic Si micromonoliths as microreformers to generate hydrogen from the SR of different fuels to power portable fuel cells.