Effect of ball-milling and Fe-/Al-doping on the structural aspect and visible light photocatalytic activity of TiO2 towards Escherichia coli bacteria abatement.

Abstract Escherichia coli abatement was studied in liquid phase under visible light in the presence of two commercial titania photocatalysts, and of Fe- and Al-doped titania samples prepared by high energy ball-milling. The two commercial titania photocatalysts, Aeroxide P25 (Evonik industries) exhibiting both rutile and anatase structures and MPT625 (Ishihara Sangyo Kaisha), a Fe-, Al-, P- and S-doped titania exhibiting only the rutile phase, are active suggesting that neither the structure nor the doping is the driving parameter. Although the MPT625 UV–visible spectrum is shifted towards the visible domain with respect to the P25 one, the effect on bacteria is not increased. On the other hand, the ball milled iron-doped P25 samples exhibit low activities in bacteria abatement under visible light due to charge recombinations unfavorable to catalysis as shown by photoluminescence measurements. While doping elements are in interstitial positions within the rutile structure in MPT625 sample, they are located at the surface in ball milled samples and in isolated octahedral units according to 57 Fe Mossbauer spectrometry. The location of doping elements at the surface is suggested to be responsible for the sample cytotoxicity observed in the dark.