An electrical characterization of a two-dimensional electron gas in GaN/AlGaN on silicon substrates

We present results of transport measurements performed on AlGaN/GaN heterostructures grown on silicon substrates. Variable temperature Hall effect measurements revealed that the temperature dependence of the carrier density and mobility were characteristic of a two-dimensional electron gas (2DEG). Carrier densities greater than 1×1013 cm−2 and Hall mobilities in excess of 1500 cm2/V s were measured at room temperature. Variable field Hall measurements at low temperatures, and in magnetic fields up to 6 T, indicated that conduction is dominated by a single carrier type in these samples. Shubnikov–de Haas (SdH) measurements were also performed, but no oscillations were observed in fields up to 8 T and at temperatures as low as 1.2 K. Illuminating some of the samples with a blue (λ=470 nm) light emitting diode (LED) induced a persistent increase in the carrier density. SdH measurements were repeated and again no oscillations were present following illumination. However, exposing the samples to radiation from...