POLYMER SOLID ELECTROLYTES BASED ON ETHYLENE OXIDE COPOLYMERS

Ethylene oxide was copolymerized with propylene oxide, epichlorohydrin or styrene oxide at various monomer feed compositions, using partially hydrolyzed organoaluminium compounds as catalysts. The copolymers obtained after doping with NaI form highly conductive polymeric electrolytes. Complex impedance measurements show relaxation semicircles much less depressed than in semicrystalline electrolytes based on Poly(ethylene oxide). The maximum values of the room temperature conductivity for each kind of copolymer containing electrolytes are higher than those for the pristine poly(ethylene oxide)-Nal system. The highest value, equal to 2.6 · 10−5 S/cm at 25°C, was found for poly(ethylene oxide-co-propylene oxide) containing 33 mol-% of propylene oxide monomeric units. Ethylenoxid wurde mit Propylenoxid, Epichlorhydrin und Styroloxid bei verschiedenen Comonomerzusammensetzungen unter Verwendung partiell hydrolysierter Organoaluminiumverbindungen copolymerisiert. Die so erhaltenen Copolymeren zeigten nach der Dotierung mit NaI eine hohe elektrische Leitfahigkeit. Impedanzmessungen dieser dotierten Copolymeren zeigten eine weit geringere Dampfung der Relaxationshalbkreise als bei semikristallinen Leitern aus Poly(ethylenoxid). Die maximale Leitfahigkeit der dotierten Copolymeren war bei Raumtemperatur in jedem Fall hoher als die des homopolymeren Poly(ethylenoxid)-NaI-Systems. Der hochste Leitfahigkeitswert (2,6 · 10−5 S/cm bei 25°C) wurde bei einem Ethylenoxid-Propylenoxid-Copolymeren mit 33 mol-% Propylenoxid gemessen.