Lead-Bismuth Eutectic Corrosion Behaviors of Ferritic/Martensitic Steels in Low Oxygen Concentration Environment

In order to investigate the compatibility of candidate structural materials with liquid metals, two kinds of ferritic/martensitic steels were chosen to contact with lead–bismuth eutectic in sealed quartz–glass tubes. The corrosion exposures were for 500 and 3000 h. Results showed that the oxidation layer and carbide dissolution layer on the two steels grew with contact time under oxygen unsaturated condition. Short-term corrosion behavior of a newly developed steel showed better lead–bismuth eutectic corrosion resistance than T91 at 873 K.